Dimensiones, pondus theoreticum, et parametri physici tuborum ferreorum quadratorum

Tabula A, Pondus theoreticum et parametri physici dimensionum pro tubis ferreis quadratis

-Basic dimensiones Cros-Lorem area Theoretical pondus Momentum inertiae section modulus
A S F G Jx-Jy Wx-Wy
MM c㎡ kg/m² cm⁴ cm3
12 0.8 0.347 0.273 0.072 0.119
1 0.423 0.332 0.084 0.140
14 1 0.503 0.395 0.139 0.199
1.5 0.711 0.558 0.181 0.259
16 1 0.583 0.458 0.216 0.270
1.5 0.831 0.653 0.286 0.357
18 1 0.663 0.520 0.315 0.351
1.5 0.951 0.747 0.424 0.471
2 1.211 0.951 0.505 0.561
20 1 0.743 0.583 0.442 0.442
1.5 1.071 0.841 0.601 0.601
2 1.371 1.076 0.725 0.725
2.5 1.643 1.290 0.817 0.817
22 1 0.823 0.646 0.599 0.544
1.5 1.191 0.935 0.822 0.748
2 1.531 1.202 1.001 0.910
2.5 1.843 1.447 1.140 1.036
25 1.5 1.371 1.077 1.246 0.997
2 1.771 1.390 1.535 1.228
2.5 2.143 1.682 1.770 1.416
3 2.485 1.951 1.955 1.564
30 2 2.171 1.704 2.797 1.865
3 3.085 2.422 3.670 2.447
3.5 3.500 2.747 3.996 2.664
4 3.885 3.050 4.256 2.837
32 2 2.331 1.830 3.450 2.157
3 3.325 2.611 4.569 2.856
3.5 3.780 2.967 4.999 3.124
4 4.205 3.301 5.351 3.344
35 2 2.571 2.018 4.610 2.634
3 3.685 2.893 6.176 3.529
3.5 4.200 3.297 6.799 3.885
4 4.685 3.678 7.324 4.185
36 2 2.651 2.081 5.048 2.804
3 3.805 2.987 6.785 3.769
4 4.845 3.804 8.076 4.487
5 5.771 4.530 8.975 4.986
40 Duo 2.971 2.332 7.075 3.537
Tres 4.285 3.364 9.622 4.811
quattuor 5.485 4.306 11.60 5.799
quinque 6.571 5.158 13.06 6.532
42 2 3.131 2.458 8.265 3.936
3 4.525 3.553 11.30 5.380
4 5.805 4.557 13.69 6.519
5 6.971 5.472 15.51 7.385
45 Duo 3.371 2.646 10.29 4.574
Tres 4.885 3.835 14.16 6.293
quattuor 6.285 4.936 17.28 7.679
quinque 7.571 5.943 19.72 8.763
quinquaginta Duo 3.771 2.960 14.36 5.743
Tres 5.485 4.306 19.94 7.975
quattuor 7.085 5.562 24.56 9.826
quinque 8.571 6.728 28.32 11.33
55 2 4.171 3.274 19.38 7.046
3 6.085 4.777 27.11 9.857
4 7.885 6.190 33.66 12.24
5 9.571 7.513 39.11 14.22
sexaginta Tres 6.685 5.248 35.82 11.94
quattuor 8.685 6.818 44.75 14.92
quinque 10.57 8.298 52.35 17.45
sex 12.34 9.688 58.72 19.57
65 3 7.285 5.719 46.22 14.22
4 9.485 7.446 58.05 17.86
5 11.57 9.083 68.29 XXI.I
6 13.54 10.63 77.03 23.70
70 3 7.885 6.190 58.46 16.70
4 10.29 8.074 73.76 XXI.VIII
5 12.57 9.868 87.18 24.91
6 14.74 11.57 98.81 28.23
75 4 11.09 8.702 92.08 24.55
5 13.57 10.65 109.3 29.14
6 15.94 12.51 124.4 33.16
8 19.79 15.54 141.4 37.72
80 4 11.89 9.330 113.2 28.30
5 14.57 11.44 134.8 33.70
6 17.14 13.46 154.0 38.49
8 21.39 16.79 177.2 44.30
90 4 13.49 10.59 164.7 36.59
5 16.57 13.01 197.2 43.82
6 19.54 15.34 226.6 50.35
8 24.59 19.30 265.8 59.06
centum 5 18.57 14.58 276.4 55.27
6 21.94 17.22 319.0 63.80
8 27.79 21.82 379.8 75.95
10 33.42 XXVI.XXIV 432.6 86.52
108 5 20.17 15.83 353.1 65.39
6 23.86 18.73 408.9 75.72
8 30.35 23.83 491.4 91.00
10 36.62 28.75 564.3 104.5
CXX 6 26.74 20.99 573.1 95.51
8 34.19 26.84 696.8 116.1
10 41.42 32.52 807.9 134.7
12 48.13 37.78 897.0 149.5
125 6 27.94 21.93 652.7 104.4
8 35.79 28.10 797.0 127.5
10 43.42 34.09 927.2 148.3
12 50.53 39.67 1033.2 165.3
130 6 29.14 22.88 739.5 113.8
8 37.39 29.35 906.3 139.4
10 45.42 35.66 1057.6 162.7
12 52.93 41.55 1182.5 181.9
140 6 31.54 24.76 935.3 133.6
8 40.59 31.86 1153.9 164.8
10 49.42 38.80 1354.1 193.4
12 57.73 45.32 1522.8 217.5
CL 8 43.79 34.38 1443.0 192.4
10 53.42 41.94 1701.2 226.8
12 62.53 49.09 1922.6 256.3
14 71.11 55.82 2109.2 281.2
CLX 8 46.99 36.89 1776.7 222.1
10 57.42 45.08 2103.1 262.9
12 67.33 52.86 2386.8 298.4
14 76.71 60.22 2630.1 328.8
CLXXX 8 53.39 41.91 2590.7 287.9
10 65.42 51.36 3086.9 343.0
12 76.93 60.39 3527.6 392.0
14 87.91 69.01 3915.3 435.0
ducenti 10 73.42 57.64 4337.6 433.8
12 86.53 67.93 4983.6 498.4
14 99.11 77.80 5562.3 556.2
16 111.2 87.27 6076.4 607.6
250 10 93.42 73.34 8841.9 707.3
12 110.5 86.77 10254.2 820.3
14 127.1 99.78 11556.2 924.5
16 143.2 112.4 12751.4 1020.1
280 10 105.4 82.76 12648.9 903.5
12 124.9 98.07 14726.8 1051.9
14 143.9 113.0 16663.5 1190.2
16 162.4 127.5 18462.8 1318.8
Cum S<=6 mm, R-1.5S, formula commendata ad pondus theoriae administrationis quadratae computandum in aequatione (A1) ostenditur;
Cum S > 6mm, R = 2S, formula commendata ad pondus theoriae administrationis quadratae computandum in aequatione (A2) ostenditur.
G=0.015 7S (2A-2.858 4S) (A1)
G=0.015 7S (2A-3.287 6S) (A2)
In formula:
G - Pondus theoreticum tubi ferrei quadrati (densitatis 7.85 kg/dm3), in chiliogrammatibus per metrum (kg/m);
A - Longitudo lateris tubi ferrei quadrati, in millimetris (mm)
S - crassitudo nominalis parietis tubi ferrei quadrati, in millimetris (mm)

 

 

 

Tempus publicationis: Die XXVIII mensis Iunii, anno MMXXIII